| Specification |
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: SiO2, SiC, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Standard Density: 6, 8, 10 Lbs./Cu. FT. (96, 128, 160 Kg/M3);
Size: 7320 * 610/1220 * 25mm, 3660 * 610;
Standard Width: 24" and 48" (610/1220mm);
Standard Thickness: 1/4", 1/2", 1", 1-1/2", 2" (6/12.7/25/38/50mm);
Features: No Asbestos, Low Thermal Conductivity etc;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivitycompression Rebound: ≤ 0.153;
Raw Material: Ceramic Fibre Bulk;
Color: White;
Application: Refractory;
Feature: Heat Resistant Insulation;
Classification Temperature: 1260;
Thermal Conductivity: >90;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material;
Temprature Classification: 1900℃, 1600℃, 1500℃, 1400℃, 1260℃, 1050℃, 2200℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3, Zro2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Jilt Silk Rug;
Kind: Zirconia Fiber;
Zro2 +Hfo2(%): 89.74;
Y203(%): 10.06;
Pellet Content≥75μ(%): <2;
Appearance: White, Cotton Wool;
Mean Diameter: 200nm-400nm/800nm-1um/2-4um;
Fibrous Phase: Tetragonal;
Service Temperature: ≤2200℃;
Fusing Point: >2700℃;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Chunking;
Manufacturing Technique: Blowing Spun;
Kind: Chrome+Zirconium;
Product Name: Ceramic Fiber Module;
Type: 1500c Chromium Zirconium Composite;
Classification Temperature: 1500c;
Product Keywords: Heat-Insulating;
Advantage: Regular Size, Easy to Install;
Color: Green and White;
Raw Material: Ceramic Fiber;
Length: as Per Customer's Request;
Width: as Per Customer's Request;
Thickness: as Per Customer's Request;
Bulk Density: 170-260(Kg/M3);
Design According to Drawing: Support;
Sample: Support;
Application: Refractory Furnace Lining Insulation Materials;
Feature: Low Thermal Conductivity;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Chunking;
Manufacturing Technique: Blowing Spun;
Kind: Chrome+Zirconium;
Product Name: Ceramic Fiber Module;
Type: 1500c Chromium Zirconium Composite;
Classification Temperature: 1500c;
Product Keywords: Heat-Insulating;
Advantage: Regular Size, Easy to Install;
Color: Green and White;
Raw Material: Ceramic Fiber;
Length: as Per Customer's Request;
Width: as Per Customer's Request;
Thickness: as Per Customer's Request;
Bulk Density: 170-260(Kg/M3);
Design According to Drawing: Support;
Sample: Support;
Application: Refractory Furnace Lining Insulation Materials;
Feature: Low Thermal Conductivity;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Chunking;
Manufacturing Technique: Blowing Spun;
Kind: Chrome+Zirconium;
Product Name: Ceramic Fiber Module;
Type: 1500c Chromium Zirconium Composite;
Classification Temperature: 1500c;
Product Keywords: Heat-Insulating;
Advantage: Regular Size, Easy to Install;
Color: Green and White;
Raw Material: Ceramic Fiber;
Length: as Per Customer's Request;
Width: as Per Customer's Request;
Thickness: as Per Customer's Request;
Bulk Density: 170-260(Kg/M3);
Design According to Drawing: Support;
Sample: Support;
Application: Refractory Furnace Lining Insulation Materials;
Feature: Low Thermal Conductivity;
|