| Specification |
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Application: Fourdry Industry Bottom Poring System;
Bulk Density: 2100-2350 Kg/M3;
Features: Low Sticking of Refractory and Steel After Use;
Cold Crushing Strength: 30 - 40 MPa;
Type: Molten Steel Pouring Control Material;
Material: Flint Clay, Bauxite, Andalusite, Mullite;
|
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Al2O3: 45% ;60%;70%;
Fe2o3: 0.8-1.6%Max;
TiO2: 2-2.8%;
K2o: 0.1-1.5%;
Density: 2.4-2.8g/cm3;
Mullite Phase: 80-90;
Refracotry Temperature: 1790-2200;
Grade: M45;M60;M70;
Type: Refractory Material;
Material: Mullite;
|
Feature: Long Time Materials, Instant Materials, Firebrick;
Refractoriness (℃): Refractoriness> 2000;
Shape: Block;
Product Name: Chromium Corundum Fire Brick for Gasifier Furnace;
Apparent Porosity: 20.0-22.0;
Bulk Density(Kg/M3): 2.9-3.8g /Cm3;
Cold Crushing Strength(MPa): 40~70MPa;
Advantage: Thermal Shock Resistance;
Keyword: Refractory Chrome Corundum Brick;
Application: Blast Furnace, Glass Kiln, Cement Kiln and So on;
Al2O3 Content (%): 48%-85%;
Raw Material: Zircon Sand;
Processing Service: Punching, Cutting, Moulding;
Type1: Fire Brick;
Type: Heat-Resistant Material;
Material: China High Alumina Brick;
|
Feature: Long Time Materials, Instant Materials, Firebrick;
Refractoriness (℃): Refractoriness> 2000;
Shape: Block;
Product Name: Fused Chrome Corundum Brick;
Apparent Porosity: 20.0-22.0;
Bulk Density(Kg/M3): 2.9-3.8g /Cm3;
Cold Crushing Strength(MPa): 40~70MPa;
Advantage: Thermal Shock Resistance;
Keyword: Refractory Chrome Corundum Brick;
Application: Blast Furnace, Glass Kiln, Cement Kiln and So on;
Al2O3 Content (%): 48%-85%;
Raw Material: Zircon Sand;
Processing Service: Punching, Cutting, Moulding;
Type1: Fire Brick;
Type: Heat-Resistant Material;
Material: China High Alumina Brick;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Block;
Model No.: Porous Brick;
Workmanship: High Temp. Deep Burnt;
Apparent Porosity: 26.0~30.0;
Density: 2.65~2.80g/cm3;
Application: Ladle Casting in Steel Plants;
Application1: Ladle Casting in Steel Plants;
Sintering Temperature: 1500-1600c;
Package: Long Distance Seaworthy Wooden Crate;
Delivery Time: 60-70 Days;
Type of Product: Semi Finished;
Departure Port: Qingdao, China;
Aftersale Service: Available;
Keywords: Purging Plugs for Steel Ladle Bottom;
Formula: Tabular Alumina+Corundum;
on Site Checking: Available;
|