| Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃, 650℃;
Chemical Composition:: Calcium, Magnesium, Silicate Chemistry;
Shape: Braid Rope;
Manufacturing Technique: Spray Silk Rug;
Kind: Bio-Soluble Fiber;
Color: Green;
Standard Densities: 600-650 Kg/M3;
Reinforced Material: Fiberglass or Stainless Steel;
Customized Service: Yes, Width/Thickness Can Be Customized;
Thermal Shock Resistance: Good;
Features: Light Weight, Low Heat Storage, etc.;
Application: Gaskets, Seals, Pipe Wrap, etc.;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Width: 610mm/1220mm;
Length: 7200mm, 3600mm etc;
Density: 96kg/M3, 128kg/M3;
Temperature: 1050c, 1260c, 1430 C;
Color: White;
Melting Point: 1760c;
Tensile Strength: >30kpa;
Fiber Diameter (Um): 3-5;
Shrinkage (24 Hours ): ≤2.5 (1000°c);
Shot Content (Φ≥0.212mm) (%): <15;
Thermal Conductivity (W/M·K): 0.035-0.18;
Shapes: Any Shape Can Be Cut;
Smell: No Smell;
Inorganic: No Binder;
Refractory Grade: Fireproof;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Length: 1200mm;
Width: 1000mm;
Min Thickness: 3mm;
Std Thickness: 10mm 12mm 15mm 20mm 25mm 30mm 50mm 100mm;
Density: 220kg/M3 -350kg/M3;
Color: White;
Shapes: Can Be Cut to Any Shapes;
Loss of Ignition, Loi, %: <8%;
Types: Inroganic Type and Organic Type;
Shrinkage, %,: <3;
Compressive Strength,: >0.2;
Thermal Conductivity, W/M•K: 0.03-0.18;
Grad: Bio Soluble;
Refractory Grade: Non-Inflammable;
Application: Oven, Furnace, Boiler, Stove Heat Insulation Liner;
|