| Specification |
Feature: Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Size(Shapes): Straights, Arch, Wedge, Soaps, Splits...;
Density: 2250-2650 Kg/M3;
Features: Fire/Alkalis Resistant, Lower Shrinkage, etc.;
Thermal Shock Resistant: Extremely;
Type: Refractory Material;
Material: Bauxite;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80;
Fe2o3: ≤2.8;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700℃;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55 Ha65 Ha70 Ha75 Ha80;
Refractoriness Under Load (0.2MPa): 1430-1700 ℃;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80;
Fe2o3: ≤2.8;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700℃;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55 Ha65 Ha70 Ha75 Ha80;
Refractoriness Under Load (0.2MPa): 1430-1700 ℃;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80;
Fe2o3: ≤2.8;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55 Ha65 Ha70 Ha75 Ha80;
Refractoriness Under Load (0.2MPa): 1430-1700 ºC;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80;
Fe2o3: ≤2.8;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700℃;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55 Ha65 Ha70 Ha75 Ha80;
Refractoriness Under Load (0.2MPa): 1430-1700 ℃;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|