| Specification |
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry, Non-Ferrous Metal Smelting;
Carbon Content: High-Carbon;
Customization: Yes;
Expansion Ratio: >300Ml/G;
Grain Size: 177μm;
Feature: High Performance;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|