| Specification |
Application: Chemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Forming Way: Molded Graphite; Isostatic Graphite;
Ash Content: ≤0.07%;
Compress Strength: ≥50-90 MPa;
Bulk Density: ≥1.70-1.88 G/Cc;
Specific Resistivity: ≤9-13 μΩ*M;
Flexural Strength: ≥25-42 MPa;
Package: Custom Packing;
Product Name: Molded Graphite Block;
Material: High Purity Graphite;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|