| Specification |
Material: Al-Zr-C;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Usage: Steel Industry;
Al2O3 %: 85%;
C%: 2.5%;
B.D(≥g/cm3): 2.9;
a.P.P(≤%): 12;
C.C.S(≥MPa): 100;
|
Material: Microporous Foam Ceramic;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Board;
Usage: Aerospace, Ceramic Industry, Energy Industry, Glass Industry, Non-Metallic Mineral Processing Industry, Scientific Research and Experiments, Steel Industry;
Crystalline Phase: Corundum/Mullite;
Volume Density: 0.4~0.6g/Cm³;
Maximum Use Temperature: 1800℃;
Long-Term Use Temperature: 1750℃;
Permanent Linear Change on Heating: ≤±0.5%(1750℃*3h);
|
Material: Microporous Foam Ceramic;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Board;
Usage: Aerospace, Ceramic Industry, Energy Industry, Glass Industry, Non-Metallic Mineral Processing Industry, Scientific Research and Experiments, Steel Industry;
Crystalline Phase: Corundum/Mullite;
Volume Density: 0.4~0.6g/Cm³;
Maximum Use Temperature: 1800℃;
Long-Term Use Temperature: 1750℃;
Permanent Linear Change on Heating: ≤±0.5%(1750℃*3h);
|
Material: Microporous Foam Ceramic;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Board;
Usage: Aerospace, Ceramic Industry, Energy Industry, Glass Industry, Non-Metallic Mineral Processing Industry, Scientific Research and Experiments, Steel Industry;
Crystalline Phase: Corundum/Mullite;
Volume Density: 0.4~0.6g/Cm³;
Maximum Use Temperature: 1800℃;
Long-Term Use Temperature: 1750℃;
Permanent Linear Change on Heating: ≤±0.5%(1750℃*3h);
|
Material: Microporous Foam Ceramic;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Board;
Usage: Aerospace, Ceramic Industry, Energy Industry, Glass Industry, Non-Metallic Mineral Processing Industry, Scientific Research and Experiments, Steel Industry;
Crystalline Phase: Corundum/Mullite;
Volume Density: 0.4~0.6g/Cm³;
Maximum Use Temperature: 1800℃;
Long-Term Use Temperature: 1750℃;
Permanent Linear Change on Heating: ≤±0.5%(1750℃*3h);
|