| Specification |
Feature: Corrosion Resistance, Good Insulation Performance, Thermal Shock Resistance;
Production Process: Pressing Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Material: Mg-C Material, Alumina Material;
Customizable: Yes;
MGO: 80%;
C: 10%;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Deep Fired;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Corundum Refractory CS2 Ladle Sliding Gate Plate F;
Materials: Al2O3 Zro2 C or Al C;
Al2O3: 85% Min;
Zro2: 4% Min;
C: 3% Min;
Fire Process: Burned;
Finish Product: with Steel Can and Belt;
Semi-Finished Products: Available;
Rough Brick: Available;
Application: Continuous Casting Flow Control;
Usage Area: Steel Iron Industry;
Function: Control The Flow Rate of Molten Steel;
Type: Steel Making Ladle Bottom Refractory;
Slide Gate Mechansim: Available;
Service Life Performance: 4-8 Times;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Deep Fired;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: S2 Alumina Zirconia Carbon Bonded Refractory Ladle;
Materials: Al2O3 Zro2 C or Al C;
Al2O3: 85% Min;
Zro2: 4% Min;
C: 3% Min;
Fire Process: Burned;
Finish Product: with Steel Can and Belt;
Semi-Finished Products: Available;
Rough Brick: Available;
Application: Continuous Casting Flow Control;
Usage Area: Steel Iron Industry;
Function: Control The Flow Rate of Molten Steel;
Type: Steel Making Ladle Bottom Refractory;
Slide Gate Mechansim: Available;
Service Life Performance: 4-8 Times;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Ls70 Steel Making Alumina Carbon Ladle Slide Gate;
Material: Al-Zr-C or Al-C;
Brand: Sinorefractory /Snref;
Main Element: Alumina&Zirconia&Carbon;
Application: Ladle of Steel Mill;
Process: Shaped-Dry-High Temperature Firing-Pitch Immersed-;
Flatness of Sliding Surface: Less Than 0.05mm;
Feature 1: High Mechanical Strength;
Feature 2: High Resistance;
Feature 3: Excellent Oxidation Resistance;
Feature 5: Good Thermal Shock Stability;
Service Life: 4-8 Heats;
Usage Area: Continuous Casting in Steel Plant;
Workmanship: High Temperature Deep Burnt;
Other Material Type: Al-C or MGO Spinel Slide Plates;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Casting High Temperature Firing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Product Name: Segment Porous Purging Plug for Steel Refining;
Type 1: Slit/Slot Type Purge Plug;
Type 2: Porous Purge Plug;
Type 3: Segment /Plate Purge Plug;
Type 4: Preassembled Purge Plug and Well Block;
Types: Cleaning Plugs and Related Systems;
Metallurgical Needs: Different Refining Processes (Rh, Lf, Vd, VOD, Va;
Raw Material of Slit Type: Chromite Corundum Spinel or Corundum Spinel;
Main Feature: High Blowing Rate;
Advantage: Easyier for Operation Control During Refining Proc;
Flow Rate Range: 12%-20%;
Al2O3/(%) Content: Not Less Than 85%;
Al2O3+MGO+Cr2o3 /(%): Not Less Than 93%;
Bubulk Density/(g/cm3): Not Lower Than 3.0;
Application: Core Components for Refining and Post-Furnace Trea;
|