| Specification |
Material: Al-Zr-C;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Al2O3 %: 85%;
C%: 2.5%;
B.D(≥g/cm3): 2.9;
a.P.P(≤%): 12;
C.C.S(≥MPa): 100;
Feature: Long Time Materials;
Type: Refractory Material;
|
Material: Pure Zirconium;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Customized;
Usage: Aerospace, Ceramic Production, Chemical Industry, Environmental Protection Equipment, Glass Manufacturing, Industrial Kilns, Petroleum Refining, Steel Smelting;
Zirconium Content: 30%<Zirconium Content<65%;
Recommended Maximum Service Temperature: 1800-2200;
Permanent Linear Change (1600°C × 2h, %): 0.1-0.5;
Crystalline Phase: Cubic Zirconia;
Appearance: White, Rigid, Smooth Surface, No Damage;
|
Material: Pure Zirconium;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Customized;
Usage: Aerospace, Ceramic Production, Chemical Industry, Environmental Protection Equipment, Glass Manufacturing, Industrial Kilns, Petroleum Refining, Steel Smelting;
Zirconium Content: 30%<Zirconium Content<65%;
Recommended Maximum Service Temperature: 1800-2200;
Permanent Linear Change (1600°C × 2h, %): 0.1-0.5;
Crystalline Phase: Cubic Zirconia;
Appearance: White, Rigid, Smooth Surface, No Damage;
|
Material: Pure Zirconium;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Customized;
Usage: Aerospace, Ceramic Production, Chemical Industry, Environmental Protection Equipment, Glass Manufacturing, Industrial Kilns, Petroleum Refining, Steel Smelting;
Zirconium Content: 30%<Zirconium Content<65%;
Recommended Maximum Service Temperature: 1800-2200;
Permanent Linear Change (1600°C × 2h, %): 0.1-0.5;
Crystalline Phase: Cubic Zirconia;
Appearance: White, Rigid, Smooth Surface, No Damage;
|
Material: Pure Zirconium;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Customized;
Usage: Aerospace, Ceramic Production, Chemical Industry, Environmental Protection Equipment, Glass Manufacturing, Industrial Kilns, Petroleum Refining, Steel Smelting;
Zirconium Content: 30%<Zirconium Content<65%;
Recommended Maximum Service Temperature: 1800-2200;
Permanent Linear Change (1600°C × 2h, %): 0.1-0.5;
Crystalline Phase: Cubic Zirconia;
Appearance: White, Rigid, Smooth Surface, No Damage;
|