| Specification |
Feature: Corrosion Resistance, Thermal Shock Resistance, Good Errosion Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Application Temperature: 1700;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Casting High Temperature Firing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Powder;
Particle Size: 1-1.5 mm;
Bulk Density: Bulk Density;
Application: Steel Making Ladle Nozzle;
Opening Rate: 95% 98% 99%;
Feature1: Good Liquidity;
High Quality: Effectively Prevent Molten Steel Penetration;
Raw Material: High Purity Chromium Ores or Compounds Containing;
Effect: Ladle Flows Into Tundish;
Specification1: NFC-Si;
Production Capacity1: 10 000 0 Tons/Year;
|
Feature: Molten Metal Filtration;
Refractoriness (℃): 1500 Celsius;
Shape: Plate;
Size: 35mm-200mm;
Csi: 50/100/200/300;
Application: Gray Iron, Ductile Iron, Copper, Brass, Aluminum;
Compressive Strength: 20MPa;
Shapes: Round, Square and Rectangle;
Size Tolerance: -1mm ~1mm;
Type: Refractory Material;
Material: Mullite;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Casting High Temperature Firing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Product Name: Slot Purging Plug with Well Block Refractory Brick;
Type 1: Slit/Slot Type Purge Plug;
Type 2: Porous Purge Plug;
Type 3: Segment /Plate Purge Plug;
Type 4: Preassembled Purge Plug and Well Block;
Types: Cleaning Plugs and Related Systems;
Metallurgical Needs: Different Refining Processes (Rh, Lf, Vd, VOD, Va;
Raw Material of Slit Type: Chromite Corundum Spinel or Corundum Spinel;
Main Feature: High Blowing Rate;
Advantage: Easyier for Operation Control During Refining Proc;
Flow Rate Range: 12%-20%;
Al2O3/(%) Content: Not Less Than 85%;
Al2O3+MGO+Cr2o3 /(%): Not Less Than 93%;
Bubulk Density/(g/cm3): Not Lower Than 3.0;
Application: Core Components for Refining and Post-Furnace Trea;
|
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Flocon 6300 Ladle Sliding Gate Plate Continuous;
Advantage: Long Life Service;
Application: Eaf or Bof Furnace Ladle Bottom;
MGO Content: Not Less Than 83%;
Al2O3 Content: Not Higher Than 12%;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Function: Control The Flow of Molten Steel in Continuous;
Pre-Assemble: Available;
Feature 1: High Temperature Resistance:;
Feature 2: Good Wear Resistance;
Feature 3: Precise Control Performance;
Flatness: Not More Than 0.05mm;
Matching with: Slide Gate Mechanism System;
Use Area: Slide Gate Valve in Steel Making;
|