| Specification |
Feature: Corrosion Resistance, Good Insulation Performance, Thermal Shock Resistance;
Production Process: Pressing Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Al2O3 %: 85%;
C%: 2.5%;
B.D(≥g/cm3): 2.9;
a.P.P(≤%): 12;
C.C.S(≥MPa): 100;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, High Mechanical Strength, Thermal Shock Resistance;
Al2O3: 90%;
Sio2: 9%;
Fe2o3: 0.5%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
|
Feature: Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Product Name: Mullite Insulation Bircks;
Cold Compressive Strength: 1.2-2.5 MPa;
Bulk Density: 0.55-1.03 g/cm3;
Fe2o3: Max 1.0%;
Softening Temperature Under Load: More Than 1420;
Apparent Porosity (%): More Than 62%;
Usage: Glass Furnace, Steel Converter .etc;
Price: Factory Outlets;
Keyword: Light Weight Insulation Mullite Bricks Sta;
Samples: Provide;
Keyword 1: Insulation Brick;
Type: Refractory Material;
Material: Mullite;
|
Feature: Feature: Good Thermal Shock Resistance;
Refractoriness (℃): Refractoriness> 2000;
Shape: Silicon Carbide Sagger/Tank;
Product Name: Silicon Carbide Sagger;
Brand Name: Rongsheng;
Density: 2.8g/cm3;
Service Life: 150 Times;
Size: Customizable;
Attribute: High Temperature Resistance;
Usage: Kiln Car of Ceramic Kiln;
Keyword: Silicon Carbide Sagger;
Sic Content: 98% or Custom;
OEM: Yes;
Raw Material: Silicon Carbide (Sic);
Material: Silicon Carbide (SiC);
Type: Silicon Carbide Sagger;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Pressing;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: High Temperature Burned Ladle Sliding Gate Plate C;
Material: Al2O3+Zro2+C;
Brand: Sinorefractory /Snref;
Main Element: Alumina&Zirconia&Carbon;
Application: Ladle of Steel Mill;
Process: Shaped-Dry-High Temperature Firing-Pitch Immersed-;
Flatness of Sliding Surface: Less Than 0.05mm;
Feature 1: High Mechanical Strength;
Feature 2: High Resistance;
Feature 3: Excellent Oxidation Resistance;
Feature 5: Good Thermal Shock Stability;
Service Life: 4-8 Heats;
Usage Area: Continuous Casting in Steel Plant;
Workmanship: High Temperature Deep Burnt;
Other Material Type: Al-C or MGO Spinel Slide Plates;
|