| Specification |
Feature: Corrosion Resistance, Good Insulation Performance, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Al2O3 %: 85%;
C%: 2.5%;
B.D(≥g/cm3): 2.9;
a.P.P(≤%): 12;
C.C.S(≥MPa): 100;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Casting High Temperature Firing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Product Name: Steel Ladle Purge Plug Pre Assembly Well Block;
Type 1: Slit/Slot Type Purge Plug;
Type 2: Porous Purge Plug;
Type 3: Segment /Plate Purge Plug;
Type 4: Preassembled Purge Plug and Well Block;
Types: Cleaning Plugs and Related Systems;
Metallurgical Needs: Different Refining Processes (Rh, Lf, Vd, VOD, Va;
Raw Material of Slit Type: Chromite Corundum Spinel or Corundum Spinel;
Main Feature: High Blowing Rate;
Advantage: Easyier for Operation Control During Refining Proc;
Flow Rate Range: 12%-20%;
Al2O3/(%) Content: Not Less Than 85%;
Al2O3+MGO+Cr2o3 /(%): Not Less Than 93%;
Bubulk Density/(g/cm3): Not Lower Than 3.0;
Application: Core Components for Refining and Post-Furnace Trea;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Casting High Temperature Firing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Product Name: Slot Purging Plug Seating Well Block for Steel Mak;
Type 1: Slit/Slot Type Purge Plug;
Type 2: Porous Purge Plug;
Type 3: Segment /Plate Purge Plug;
Type 4: Preassembled Purge Plug and Well Block;
Types: Cleaning Plugs and Related Systems;
Metallurgical Needs: Different Refining Processes (Rh, Lf, Vd, VOD, Va;
Raw Material of Slit Type: Chromite Corundum Spinel or Corundum Spinel;
Main Feature: High Blowing Rate;
Advantage: Easyier for Operation Control During Refining Proc;
Flow Rate Range: 12%-20%;
Al2O3/(%) Content: Not Less Than 85%;
Al2O3+MGO+Cr2o3 /(%): Not Less Than 93%;
Bubulk Density/(g/cm3): Not Lower Than 3.0;
Application: Core Components for Refining and Post-Furnace Trea;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 90%;
Sio2: 9%;
Fe2o3: 0.5%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Deep Fired;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Ts80 Ladle Slide Gate Plate Refractory Steel Cast;
Materials: Al2O3 Zro2 C or Al C;
Al2O3: 85% Min;
Zro2: 4% Min;
C: 3% Min;
Fire Process: Burned;
Finish Product: with Steel Can and Belt;
Semi-Finished Products: Available;
Rough Brick: Available;
Application: Continuous Casting Flow Control;
Usage Area: Steel Iron Industry;
Function: Control The Flow Rate of Molten Steel;
Type: Steel Making Ladle Bottom Refractory;
Be Adapted to: Many Types of Slide Gate Mechanism System;
Formula: Adjustable;
|