| Specification |
Feature: Corrosion Resistance, Good Insulation Performance, Thermal Shock Resistance, Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Type: Refractory Material;
Material: Al-Zr-C;
Al2O3 %: 85%;
C%: 2.5%;
B.D(≥g/cm3): 2.9;
a.P.P(≤%): 12;
C.C.S(≥MPa): 100;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Ls70 Ladle Bottom Refractory Slide Gate Plate;
Material: Al2O3+Zro2+C;
Brand: Sinorefractory /Snref;
Main Element: Alumina&Zirconia&Carbon;
Application: Ladle of Steel Mill;
Process: Shaped-Dry-High Temperature Firing-Pitch Immersed-;
Flatness of Sliding Surface: Less Than 0.05mm;
Feature 1: High Mechanical Strength;
Feature 2: High Resistance;
Feature 3: Excellent Oxidation Resistance;
Feature 5: Good Thermal Shock Stability;
Service Life: 4-8 Heats;
Usage Area: Continuous Casting in Steel Plant;
Workmanship: High Temperature Deep Burnt;
Other Material Type: Al-C or MGO Spinel Slide Plates;
|
Feature: Corrosion Resistance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Deep Burnt;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Model: CS60;
Brand: Snref;
Workmanship: High Temp. Deep Burnt;
Apparent Porosity: 3-7%;
Density: 2.9-3.1 g/cm3;
Application: Ladle Casting in Steel Plants;
Working Temperature: 1500-1700c;
Package: Long Distance Seaworthy Wooden Crate;
Delivery Time: 60-70 Days;
Service Life: 4-6 Heats;
Departure Port: Qingdao, China;
Aftersale Service: Available;
Keywords: Slide Plates for Steel Ladle;
Formula: Al-C;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: CS60 Pre Assembly Mobile Ladle Slide Gate Plate Re;
Material: Al2O3+Zro2+C;
Brand: Sinorefractory /Snref;
Main Element: Alumina&Zirconia&Carbon;
Application: Ladle of Steel Mill;
Process: Shaped-Dry-High Temperature Firing-Pitch Immersed-;
Flatness of Sliding Surface: Less Than 0.05mm;
Feature 1: High Mechanical Strength;
Feature 2: High Resistance;
Feature 3: Excellent Oxidation Resistance;
Feature 5: Good Thermal Shock Stability;
Service Life: 4-8 Heats;
Usage Area: Continuous Casting in Steel Plant;
Workmanship: High Temperature Deep Burnt;
Other Material Type: Al-C or MGO Spinel Slide Plates;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Casting High Temperature Firing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Product Name: Ladle Bottom Porous Purge Plug Set Block for Steel;
Type 1: Slit/Slot Type Purge Plug;
Type 2: Porous Purge Plug;
Type 3: Segment /Plate Purge Plug;
Type 4: Preassembled Purge Plug and Well Block;
Types: Cleaning Plugs and Related Systems;
Metallurgical Needs: Different Refining Processes (Rh, Lf, Vd, VOD, Va;
Raw Material of Slit Type: Chromite Corundum Spinel or Corundum Spinel;
Main Feature: High Blowing Rate;
Advantage: Easyier for Operation Control During Refining Proc;
Flow Rate Range: 12%-20%;
Al2O3/(%) Content: Not Less Than 85%;
Al2O3+MGO+Cr2o3 /(%): Not Less Than 93%;
Bubulk Density/(g/cm3): Not Lower Than 3.0;
Application: Core Components for Refining and Post-Furnace Trea;
|