| Specification |
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Al2O3 %: 85%;
C%: 2.5%;
B.D(≥g/cm3): 2.9;
a.P.P(≤%): 12;
C.C.S(≥MPa): 100;
Type: Refractory Material;
Material: Al-Zr-C;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Cao Content %: 3;
Al203 Content (%): 45;
Si02 Content (%: 10%;
Refractoriness (Degree): Common1580< Refractoriness<1770;
Material: Alumina Cement;
Water Required for Casting %: 5-9;
Cao: 2-3%;
Bulk Densityg/Cm3): 2.4-3.0;
Ai203: 45-95%;
Application: Furnace Lining;
Fe203: 1.5-2.4;
|
Classification: Semi-Silica;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Bulk Density: 2.31~2.4G/Cm3;
Ai203 Content %): 22.5%;
Cao Content %): 2.5;
Acid Resistance: 99.8%;
Standard Size: 230*114*65mm;
Si02 Content %): 69.8%;
Si02(%): 69.8%;
High Working Temperature: 1650-1720c;
Application: Nonferrous Metal Furnace;
Single Package Size: 100X100X110.Cm;
|
Classification: Al-Zr-C;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Feature 1: High Temperature Resistance;
Feature 2: Good Wear Resistance;
Feature 3: Precise Control Performance;
Use Area: Slide Gate Valve in Steel Making;
Function: Control The Flow of Molten Steel in Continuous;
Sample Order: Acceptable;
|
Classification: Al-Zr-C;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Feature 1: High Temperature Resistance;
Feature 2: Good Wear Resistance;
Feature 3: Precise Control Performance;
Use Area: Slide Gate Valve in Steel Making;
Function: Control The Flow of Molten Steel in Continuous;
Sample Order: Acceptable;
|