| Specification |
Application: Aerospace, Electronics, Medical, Refractory, Industrial;
Purity: 95%;
Type: Ceramic Plate;
Material: Alumina;
Density: 3.6g/cm3;
Color: White;
Flexural Strength: 300 MPa;
Compressive Strength: 2300 MPa;
Thermal Conductivity: 20 W/M.K;
Dielectric Strength: >15 Kv/mm;
|
Application: Aerospace, Architectural, Ceramic Decorations, Electronics, Medical, Refractory;
Grain Size: <100nm;
Purity: 95% / 99% / 99.5% / 99.7%+ (Customizable);
Type: Ceramic Plate;
Material Composition: Aluminum Oxide (Al2O3);
Vickers Hardness: 1200-1800+ Hv;
Mohs Hardness: Grade 9;
Flexural Strength: 300-400+ MPa;
Max Service Temperature: 1350°C~1600°C;
Density: 3.6~3.9 G/Cm³;
Surface Roughness: Ra ≤ 0.2 μm;
Dimensional Tolerance: ±0.01~ ±0.05 mm (Customizable);
Color: Standard White (Gray Customizable);
Core Performance: Wear Resistant, Corrosion Resistant, High Temperat;
Application Scenarios: Customizable Per Drawings/Samples (Size, Purity, S;
Customization Service: Customizable Per Drawings/Samples (Size, Purity, S;
Service Life: 5~10 Times Longer Than Metal Rings;
|
Application: Aerospace, Architectural, Ceramic Decorations, Electronics, Medical, Refractory;
Grain Size: <100nm;
Purity: 95% / 99% / 99.5% / 99.7%+ (Customizable);
Type: Ceramic Plate;
Material Composition: Aluminum Oxide (Al2O3);
Vickers Hardness: 1200-1800+ Hv;
Mohs Hardness: Grade 9;
Flexural Strength: 300-400+ MPa;
Max Service Temperature: 1350°C~1600°C;
Density: 3.6~3.9 G/Cm³;
Surface Roughness: Ra ≤ 0.2 μm;
Dimensional Tolerance: ±0.01~ ±0.05 mm (Customizable);
Color: Standard White (Gray Customizable);
Core Performance: Wear Resistant, Corrosion Resistant, High Temperat;
Application Scenarios: Customizable Per Drawings/Samples (Size, Purity, S;
Customization Service: Customizable Per Drawings/Samples (Size, Purity, S;
Service Life: 5~10 Times Longer Than Metal Rings;
|
Application: Aerospace, Architectural, Ceramic Decorations, Electronics, Medical, Refractory;
Grain Size: <100nm;
Purity: 95% / 99% / 99.5% / 99.7%+ (Customizable);
Type: Ceramic Plate;
Material Composition: Aluminum Oxide (Al2O3);
Vickers Hardness: 1200-1800+ Hv;
Mohs Hardness: Grade 9;
Flexural Strength: 300-400+ MPa;
Max Service Temperature: 1350°C~1600°C;
Density: 3.6~3.9 G/Cm³;
Surface Roughness: Ra ≤ 0.2 μm;
Dimensional Tolerance: ±0.01~ ±0.05 mm (Customizable);
Color: Standard White (Gray Customizable);
Core Performance: Wear Resistant, Corrosion Resistant, High Temperat;
Application Scenarios: Customizable Per Drawings/Samples (Size, Purity, S;
Customization Service: Customizable Per Drawings/Samples (Size, Purity, S;
Service Life: 5~10 Times Longer Than Metal Rings;
|
Application: Aerospace, Architectural, Ceramic Decorations, Electronics, Medical, Refractory;
Grain Size: <100nm;
Purity: 95% / 99% / 99.5% / 99.7%+ (Customizable);
Type: Ceramic Plate;
Material Composition: Aluminum Oxide (Al2O3);
Vickers Hardness: 1200-1800+ Hv;
Mohs Hardness: Grade 9;
Flexural Strength: 300-400+ MPa;
Max Service Temperature: 1350°C~1600°C;
Density: 3.6~3.9 G/Cm³;
Surface Roughness: Ra ≤ 0.2 μm;
Dimensional Tolerance: ±0.01~ ±0.05 mm (Customizable);
Color: Standard White (Gray Customizable);
Core Performance: Wear Resistant, Corrosion Resistant, High Temperat;
Application Scenarios: Customizable Per Drawings/Samples (Size, Purity, S;
Customization Service: Customizable Per Drawings/Samples (Size, Purity, S;
Service Life: 5~10 Times Longer Than Metal Rings;
|