| Specification |
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry, Casting Foundry Moulding;
Carbon Content: High-Carbon;
Customization: Yes;
Compressive: 80MPa Strength;
Chemical: Composition Carbon;
Size: Customized;
Electric Resistivity: 8-10m;
Density: 1.85g/cm3;
Name: Graphite Block Blank;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, Papermaking Industry, Petrochemical Industry;
Carbon Content: High-Carbon;
Customization: Yes;
Product Name: Graphite Block;
Keywords: Carbon Graphite Block;
Grain Size≤(mm): 2-0.8;
Bulk Density(≥g/cm3): 1.6-1.72;
Compressive Strength(≥MPa): 19-35;
Flexural Strength(≥MPa): 7.8-15;
Specific Resistance(≤μωM): 9-8.5;
Ash Content (%): 0.3;
Thermal Expansivity(X10-6°C): 2-2.2;
|