| Specification |
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: Ladle Furnace Bottom Slide Gate Plate Refractory;
Type: Refractory Material;
Material 1: Al2O3-Zro2-C;
Material 2: Al2O3-C;
Al2O3: 85% Min;
Zro2: 4% Min;
C: 3% Min;
Fire Process: Burned;
Finish Product: with Steel Can and Belt;
Application: Ladle Bottom;
Function: Casting of Liquid Steel;
Life Time: 4-5 Heats;
Packing: Fumigation Free Case;
|
Classification: Semi-Silica;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Bulk Density: 2.31~2.4G/Cm3;
Ai203 Content %): 22.5%;
Cao Content %): 2.5;
Acid Resistance: 99.8%;
Standard Size: 230*114*65mm;
Si02 Content %): 69.8%;
Si02(%): 69.8%;
High Working Temperature: 1650-1720c;
Application: Nonferrous Metal Furnace;
Single Package Size: 100X100X110.Cm;
|
Classification: Semi-Silica;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Bulk Density: 2.31~2.4G/Cm3;
Ai203 Content %): 22.5%;
Cao Content %): 2.5;
Acid Resistance: 99.8%;
Standard Size: 230*114*65mm;
Si02 Content %): 69.8%;
Si02(%): 69.8%;
High Working Temperature: 1650-1720c;
Application: Nonferrous Metal Furnace;
Single Package Size: 100X100X110.Cm;
|
Classification: Semi-Silica;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Bulk Density: 2.31~2.4G/Cm3;
Ai203 Content %): 22.5%;
Cao Content %): 2.5;
Acid Resistance: 99.8%;
Standard Size: 230*114*65mm;
Si02 Content %): 69.8%;
Si02(%): 69.8%;
High Working Temperature: 1650-1720c;
Application: Nonferrous Metal Furnace;
Single Package Size: 100X100X110.Cm;
|
Classification: Semi-Silica;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Bulk Density: 2.31~2.4G/Cm3;
Ai203 Content %): 22.5%;
Cao Content %): 2.5;
Acid Resistance: 99.8%;
Standard Size: 230*114*65mm;
Si02 Content %): 69.8%;
Si02(%): 69.8%;
High Working Temperature: 1650-1720c;
Application: Nonferrous Metal Furnace;
Single Package Size: 100X100X110.Cm;
|