| Specification |
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: 1bk 2bk Ladle Sliding Gate Plate Refractory CCM;
Al2O3: 85% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Function: Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
Used for: Steel Making Molten Melting;
Formula: Ajustable;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Calcined;
Refractoriness (℃): Refractoriness> 2000;
Shape: Fepa Size, Grain Size, Powderwder;
Advantage I: Low Calorific Value, High Efficiency;
Advantage II: High Purity, Good Self-Sharpening;
High Quality: Low Na2o High B.D.;
Advantage III: High Temperature and Thermal Stability;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Corrosion Resistant;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Usage: Refractoy;
MGO Content (%: 0.01%;
Single Gross Weight: 1015.000kg;
Refractoriness (Degree): 1770<Refractoriness<2000;
Sio2 Content %: 20%~30%;
Cro Content %): 0.1~0.3%;
Single Package Size: 100X100X110.Cm;
Bulk Density: 2.75~3.1g/cm3;
Material: Alumina Block;
Sic Content (%): 1.2-1.4%;
Al203 Content %): 60%-80%;
Cold Crushing Strength: 70-90MPa;
Cao Content %): 0.34%;
Application: Industrial Furnaces;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Calcined;
Refractoriness (℃): Refractoriness> 2000;
Shape: Fepa Size, Grain Size, Powderwder;
Advantage I: Low Calorific Value, High Efficiency;
Advantage II: High Purity, Good Self-Sharpening;
High Quality: Low Na2o High B.D.;
Advantage III: High Temperature and Thermal Stability;
|
Classification: Spray Silk Rug;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Spraying Method;
Refractoriness (℃): Refractoriness<1580;
Shape: Ceramic Fiber Modules;
Usage: High Temperature Insulating Material;
Chemical Composition: Al2O3,Sio2, Al2O3+Sio2+Zro2;
Kind: Ordinary Ceramic Fiber;
Certifiacte: ISO9001,etc;
Bulk Density(g/cm3): 1.6-2.4;
Al2O3: ≥43;
Appearance: Modules;
Material: Ceramic Fiber;
Refractory Temperature: 1000-1600 Celsius;
Specifications: Customizable;
|