| Specification |
CAS No.: Not Have;
Formula: Not Have;
EINECS: Not Have;
Source: Organic Acids;
Appearance: Oily Liquid;
Grade Standard: Polyurethane Soft Foam;
Colour: Yellow;
Product Number: R.C.Z-M6;
Acid Value: Less Than or Equal<2mgkoh/G;
Hydroxyl Value: 170-220gkoh/G;
Viscosity: 800-1200GPS/25celsius;
Moisture: Less Than or Equal<0.15%;
|
CAS No.: 9016-87-9;
Formula: 9016-87-9;
EINECS: 9016-87-9;
Source: Pol/ISO;
Appearance: Liquid;
Grade Standard: Industrial Grade;
Colour: Light Yellow;
Initial Thermal: ≤0.033 W/(M•K);
Water Absorption: ≤4%;
Cream Time: 13-25;
Application: Pipe Insulation;
Highest Temperature Range: 140 ℃;
Average Cell Size: ≤0.5 mm;
Radial Cpressive Strength: ≥0.3 MPa;
Free Rise Density: 22-32;
Recommended Storage Temperature: 15~25℃;
Core Density: ≥60 Kg/M3;
Close Cell Content: ≥92;
Track Free Time: 55-90;
Polyurethane: Rigid Foam Polyurethane;
Raw Material: Raw Material;
Thermal Conductivity, 20℃: ≤0.024W/(M.K);
|
CAS No.: 9016-87-9;
Formula: 9016-87-9;
EINECS: 9016-87-9;
Source: Pol/ISO;
Appearance: Liquid;
Grade Standard: Industrial Grade;
Colour: Light Yellow;
Initial Thermal: ≤0.033 W/(M·K);
Recommended Storage Temperature: 15~25℃;
Application: Pipe Insulation;
Track Free Time: 55-90;
Radial Cpressive Strength: ≥0.3 MPa;
Water Absorption: ≤4%;
Core Density: ≥60 Kg/M3;
Highest Temperature Range: 140 ℃;
Polyurethane: Rigid Foam Polyurethane;
Free Rise Density: 22-32;
Cream Time: 13-25;
Close Cell Content: ≥92;
Average Cell Size: ≤0.5 mm;
Raw Material: Raw Material;
Thermal Conductivity, 20℃: ≤0.024W/(M.K);
|
CAS No.: 9016-87-9;
Formula: 9016-87-9;
EINECS: 9016-87-9;
Source: Pol/ISO;
Appearance: Liquid;
Grade Standard: Industrial Grade;
Colour: Light Yellow;
ISO as Some Crystallization May Occur: Above 50°c;
Application: Heat Preservation and Cold Preservation;
Lead Time: Within 3-5 Days After Payment;
ISO Stored Indoors at Temperatures: 20-30°c;
Density (25°c): 1, 08-1, 12g/cm3;
Compressive Strength: 0.12-0.20MPa;
Viscosity (25°c): 2000-2200MPa.S;
Oxygen Index: 26.0%;
MOQ: 1 Drum;
Blend Polyols Stored Indoors Tempera: 20-30°c;
ISO Avoid Storage Temperatures: Below 0°c;
Panel Material: Polyurethane Foam;
Nco Contentt%: 30, 5-31, 0;
Viscosity (25°c)Tmpa.S: 2000-2200;
Blowing Agent: Hfc-245fa, Hfo, Water;
|
CAS No.: 9016-87-9;
Formula: 9016-87-9;
EINECS: 9016-87-9;
Source: Pol/ISO;
Appearance: Liquid;
Grade Standard: Industrial Grade;
Colour: Light Yellow;
Compressive Strength(10%),Kpa: 150;
Dimensional Stability(%): Low Temperature (-30℃, 24HS) 1.0;
Hydroxyl Value Mgkoh/G: 350-450;
Dynamic Viscosity (25℃) MPa.S: 3500-4500;
Density (20℃) G/Ml: 1.1±0.02;
Storage Temperature ℃: 10-25;
Viscosity: 3500-4500;
Hydroxy Value: 350-450;
Specific Gravity: 1.05-1.10;
Blend Polyol: Part by Weight 100;
Isocynate: Part by Weight 134.4-135.6;
Density(Kg/M3): >=35;
Thermal Conductivity (10℃) W/M.K: ≤0.022;
Closed Cell Rate (%): >=90;
C-P Entane: Part by Weight 12-13;
|