| Specification |
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Product Name: Graphite Box;
Keywords: Graphite Mold;
Grain Size (≤μm): 25;
Bulk Density (≥g/cm3): 1.78-1.9;
Compressive Strength (≥MPa): 70-90;
Flexural Strength(≥MPa): 35-42;
Porosity(≤%): 17-11;
Specific Resistance(≤μωM): 12-10;
Ash Content(≤Ppm): 600-300;
Shore Hardness: 50-60;
|
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Application Area: Electronic Industry, Metal Smelting and Casting Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance, Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing and Sintering;
Apparent Density: 1.80-1.90g/cm3;
Shore Hardness: 48-50;
Electrical Strength: 10-9.5 (Ωmm2/M);
Compressive Strength: 37-42(MPa);
Flexural Strength: 78-86(MPa);
Average Pore Size: 3.2-2.4 (U M);
Coefficient of Thermal Expansion(10-6K): 4.8-4.4;
Ash (10-6K): 0.1;
Type: Graphite Mold;
Composition: Sic;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Crystal Morphology: Compact Crystalline Graphite;
|
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Application Area: Electronic Industry, Metal Smelting and Casting Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance, Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing and Sintering;
Apparent Density: 1.80-1.90g/cm3;
Shore Hardness: 48-50;
Electrical Strength: 10-9.5 (Ωmm2/M);
Compressive Strength: 37-42(MPa);
Flexural Strength: 78-86(MPa);
Average Pore Size: 3.2-2.4 (U M);
Coefficient of Thermal Expansion(10-6K): 4.8-4.4;
Ash (10-6K): 0.1;
Type: Graphite Mold;
Composition: Sic;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Crystal Morphology: Compact Crystalline Graphite;
|
Product Name: Graphite Block/ Graphite Sheet/ Graphite Material;
Compressive Strength: 40MPa;
Ash Content: 0.1%;
Bulk Density: 1.75-1.98 g/cm3;
Type: Graphite Mold;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
Forming Way: Molded Graphite/ Isostatic Graphite;
|
Sample: Available;
Type: Graphite Mold;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Composition: Graphite;
|