| Specification |
Shape: Ceramic Fiber Plate;
Temperature Grade: 1260c-1430c-1700c-1800c-1900c;
Standard Size: 900X600X 5-50mm ; 1200 X600 X25-50mm;
Density: 250-500 Kg/M3;
Delivery Time: Usually for Regular Order Within 14 Days;
Original: China Mailand;
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: SiO2, SiC, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Standard Density: 6, 8, 10 Lbs./Cu. FT. (96, 128, 160 Kg/M3);
Size: 7320 * 610/1220 * 25mm, 3660 * 610;
Standard Width: 24" and 48" (610/1220mm);
Standard Thickness: 1/4", 1/2", 1", 1-1/2", 2" (6/12.7/25/38/50mm);
Features: No Asbestos, Low Thermal Conductivity etc;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivitycompression Rebound: ≤ 0.153;
Raw Material: Ceramic Fibre Bulk;
Color: White;
Application: Refractory;
Feature: Heat Resistant Insulation;
Classification Temperature: 1260;
Thermal Conductivity: >90;
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: SiO2, SiC, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Standard Density: 6, 8, 10 Lbs./Cu. FT. (96, 128, 160 Kg/M3);
Size: 7320 * 610/1220 * 25mm, 3660 * 610;
Standard Width: 24" and 48" (610/1220mm);
Standard Thickness: 1/4", 1/2", 1", 1-1/2", 2" (6/12.7/25/38/50mm);
Features: No Asbestos, Low Thermal Conductivity etc;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivitycompression Rebound: ≤ 0.153;
Raw Material: Ceramic Fibre Bulk;
Color: White;
Application: Refractory;
Feature: Heat Resistant Insulation;
Classification Temperature: 1260;
Thermal Conductivity: >90;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Chunking;
Manufacturing Technique: 1600℃;
Kind: Containing Zirconium Ceramic Fiber;
Color: Pure White;
Application: Industrial Kilns;
Size: 300*300*300mm Can Be Customized;
Density: 160-240kg/M3;
Raw Material: Alumina Silica;
Heating Permanent Wire Shrinkage: 2%(1000ºC*24h);
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Chunking;
Manufacturing Technique: 1600℃;
Kind: Containing Zirconium Ceramic Fiber;
Color: Pure White;
Application: Industrial Kilns;
Size: 300*300*300mm Can Be Customized;
Density: 160-240kg/M3;
Raw Material: Alumina Silica;
Heating Permanent Wire Shrinkage: 2%(1000ºC*24h);
|