| Specification |
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃;
Shape: Ceramic Fiber Textile;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
City: Zibo;
Package: Carton Box or Plastic Bag;
Manufacturer: Luyang;
Raw Material: Ceramic Fiber;
Product: Ceramic Fiber Cloth;
Name: Aluminum Silicate Fiber Cloth;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃;
Chemical Composition:: Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Application: Heat Insulation;
Thickness: 10/20/30/50mm;
Width: 610-1220mm;
Length: 600/900/1000/1200mm;
Grade: HP (High Pure);
Ultimate Strength: 0.5MPa;
Working Temperature: 1100c;
Fiber Diameter: 3~5um;
Thermal Conductivitycti: 0.132(800c)/0.180(1000c);
Density: 280/300/320/350g/cm3;
Raw Material: Ceramic Fiber Bulk;
Shrinkage (1800℉, 3h): 3%(24h);
Color: Write;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: Containing Zirconium Ceramic Fiber;
Application: Refractory;
Thickness: 13-50mm;
Width: 610mm;
Length: 3600/7200/14640mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Working Temperature: 1000;
Fiber Diameter: 3-5um;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivity: ≤ 0.153;
Density (Kg/M³ ): 128;
Color: White;
Raw Material: Ceramic Fibre Bulk;
Bulk Density: 96-128kg/M3;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: Containing Zirconium Ceramic Fiber;
Application: Refractory;
Thickness: 13-50mm;
Width: 610mm;
Length: 3600/7200/14640mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Working Temperature: 1000;
Fiber Diameter: 3-5um;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivity: ≤ 0.153;
Density (Kg/M³ ): 128;
Color: White;
Raw Material: Ceramic Fibre Bulk;
Bulk Density: 96-128kg/M3;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: Containing Zirconium Ceramic Fiber;
Application: Refractory;
Thickness: 13-50mm;
Width: 610mm;
Length: 3600/7200/14640mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Working Temperature: 1000;
Fiber Diameter: 3-5um;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivity: ≤ 0.153;
Density (Kg/M³ ): 128;
Color: White;
Raw Material: Ceramic Fibre Bulk;
Bulk Density: 96-128kg/M3;
|