| Specification |
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1900℃, 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: Containing Zirconium Ceramic Fiber;
Application: Refractory;
Thickness: 13-50mm;
Width: 610mm;
Length: 3600/7200/14640mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Working Temperature: 1000;
Fiber Diameter: 3-5um;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivity: ≤ 0.153;
Density (Kg/M³ ): 128;
Color: White;
Raw Material: Ceramic Fibre Bulk;
Bulk Density: 96-128kg/M3;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: Containing Zirconium Ceramic Fiber;
Application: Refractory;
Thickness: 13-50mm;
Width: 610mm;
Length: 3600/7200/14640mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Working Temperature: 1000;
Fiber Diameter: 3-5um;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivity: ≤ 0.153;
Density (Kg/M³ ): 128;
Color: White;
Raw Material: Ceramic Fibre Bulk;
Bulk Density: 96-128kg/M3;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: Containing Zirconium Ceramic Fiber;
Application: Refractory;
Thickness: 13-50mm;
Width: 610mm;
Length: 3600/7200/14640mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Working Temperature: 1000;
Fiber Diameter: 3-5um;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivity: ≤ 0.153;
Density (Kg/M³ ): 128;
Color: White;
Raw Material: Ceramic Fibre Bulk;
Bulk Density: 96-128kg/M3;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: Containing Zirconium Ceramic Fiber;
Application: Refractory;
Thickness: 13-50mm;
Width: 610mm;
Length: 3600/7200/14640mm;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Working Temperature: 1000;
Fiber Diameter: 3-5um;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivity: ≤ 0.153;
Density (Kg/M³ ): 128;
Color: White;
Raw Material: Ceramic Fibre Bulk;
Bulk Density: 96-128kg/M3;
|