| Specification |
Density: 1.70-1.92g/cm3;
Resistivity: Less Than 12;
Compressive Strength: More Than 70MPa;
Porosity: Less Than 26%;
Elasticity Modulus  : 6-18gpa;
Thermal Expansion Coefficient: 1.47-4.25;
Temperature Resistance  : Less Than 4350 Degree;
Ash Content: Less Than 0.05%;
Type: Graphite Mold;
Carbon Content: High-Carbon;
Forming Way: Molded Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Composition: 99.9% High Purity Graphite;
Grade: High Purity Graphite;
|
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|
Application Area: Automobile Industry, Electronic Industry, Food Industry, Mould Of Plastics;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Resistivity: 9~12 Micro Ohm.M;
Clearance: 12%;
Apply: Exothermic Melting Thermite Welding;
Block Density: 1.85g/Cc Min;
Compression Strength: 85MPa Min;
Model: Yxgm150;
Material: High Pure High Density Graphite;
Surface: Polised Mirror Surface;
Special Treatment: Pyrolytic Carbon Coating Available at Request;
Advantage: Anti-Abrasion, Long Service Life;
Flexural Strength: 40 MPa Min;
Compressive Strength: 85 MPa Min;
Ash Content: 0.1% Max;
Density: 1.73G/Cm³-2.0 G/Cm³;
|