| Specification |
Material: Floating Beads;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Cup-Shaped;
Usage: Non-Metallic Mineral Processing Industry, Molten Iron Feeding;
Product: Exothermic Insulating Feeder Riser Sleeve;
Application: Cast Steel;Cast Iron;
Category: Foundry Material;
Usage2: Molten Steel Feeding;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
|
Material: Alloy/Cast Steel;
Refractoriness (℃): 500℃~1300℃;
Shape: as Customer Drawings;
Usage: Ceramic Industry, Energy Industry, Glass Industry, Non-Metallic Mineral Processing Industry, Steel Industry;
Shipping Method: by Sea, by Air, Railway, Express etc;
Quality Control: 100% Inspection;
Drawing Format: Pdf/Step/Igs/Dwg etc.;
Video Outgoing-Inspection: Provided;
Test Report: Provided;
Lead Time: Negotiable;
Factory Tour: Warm Welcome;
MOQ: 1 Piece;
Type: Heat-Resistant Material;
Outside Surface: as Cast or Machined as Per Drawing;
Heat Treatment Process: Quenching, Tempering, Normalizing, Carburizing/Nit;
|
Material: Alloy/Cast Steel;
Refractoriness (℃): 500℃~1300℃;
Shape: as Customer Drawings;
Usage: Ceramic Industry, Energy Industry, Glass Industry, Non-Metallic Mineral Processing Industry, Steel Industry;
Shipping Method: by Sea, by Air, Railway, Express etc;
Quality Control: 100% Inspection;
Drawing Format: Pdf/Step/Igs/Dwg etc.;
Video Outgoing-Inspection: Provided;
Test Report: Provided;
Lead Time: Negotiable;
Factory Tour: Warm Welcome;
MOQ: 1 Piece;
Type: Heat-Resistant Material;
Outside Surface: as Cast or Machined as Per Drawing;
Heat Treatment Process: Quenching, Tempering, Normalizing, Carburizing/Nit;
|
Material: Alumina Block;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Feature: Long Time Materials;
Type: Refractory Material;
Bulk Density(g/cm3): 3.0-3.1g/cm3;
Al2O3: 90-92%;
Cr2o3: 4-7%;
MGO: 4-7%;
Cold Crushing Strength: 90-100MPa;
Modulus of Repture: 17-20MPa;
Air Permeability (N/Min): 200-650;
|
Material: Silica Material;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Powder;
Usage: Aerospace, Ceramic Industry, Glass Industry, Non-Metallic Mineral Processing Industry, Scientific Research and Experiments, Steel Industry;
Sio2 Content (%): 70-75%;
Fe2o3 Content (%): 0.15-1.5%;
Al2O3 Content (%): 12-16%;
MGO Content (%): 0.2-0.5%;
Cao Content (%): 0.1-2%;
K2o Content (%): 1.0-1.4%;
Bulk Density: 250-400 Kg/M3;
Size: 0.1-0.3 mm;
Floating Rate: 85% Min;
Water Absorption: ≤30;
Granulation Rate: 90% Min;
Thermal Conductivity: 0.066-0.072 W/M.K;
Cylinder Compression Strength: 1.0-2.5MPa;
|