| Specification |
Feature: Long Time Materials, Instant Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Cup-Shaped;
Product: Exothermic Insulating Feeder Riser Sleeve;
Application: Cast Steel;Cast Iron;
Category: Foundry Material;
Usage: Molten Iron Feeding;
Usage2: Molten Steel Feeding;
Compressive Strength: >1.5;
Air Permeability: >30;
Generating Capacity of Heat: >3.5;
Thermal Peak: >1250;
Moisture: <1.0;
Type: Refractory Material;
Material: Alumina Cement;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Methord;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Advanced Alumina-Carbon FT160 Ladle Slide Gate PLA;
Al2O3: 85% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Function: Steel Metal Molten Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
Type: Alumina Carbon Refractory;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Methord;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Safflow Ladle Bottom Slide Gate Plate Nozzle for P;
Al2O3: 85% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Function: Steel Metal Molten Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
Type: Alumina Carbon Refractory;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Casting High Temperature Firing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Product Name: 111;
Type 1: Slit/Slot Type Purge Plug;
Type 2: Porous Purge Plug;
Type 3: Segment /Plate Purge Plug;
Type 4: Preassembled Purge Plug and Well Block;
Types: Cleaning Plugs and Related Systems;
Metallurgical Needs: Different Refining Processes (Rh, Lf, Vd, VOD, Va;
Raw Material of Slit Type: Chromite Corundum Spinel or Corundum Spinel;
Main Feature: High Blowing Rate;
Advantage: Easyier for Operation Control During Refining Proc;
Flow Rate Range: 12%-20%;
Al2O3/(%) Content: Not Less Than 85%;
Al2O3+MGO+Cr2o3 /(%): Not Less Than 93%;
Bubulk Density/(g/cm3): Not Lower Than 3.0;
Application: Core Components for Refining and Post-Furnace Trea;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Casting High Temperature Firing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Product Name: Snref Refractory Ladle Gas Purging System Purge Pl;
Type 1: Slit/Slot Type Purge Plug;
Type 2: Porous Purge Plug;
Type 3: Segment /Plate Purge Plug;
Type 4: Preassembled Purge Plug and Well Block;
Types: Cleaning Plugs and Related Systems;
Metallurgical Needs: Different Refining Processes (Rh, Lf, Vd, VOD, Va;
Raw Material of Slit Type: Chromite Corundum Spinel or Corundum Spinel;
Main Feature: High Blowing Rate;
Advantage: Easyier for Operation Control During Refining Proc;
Flow Rate Range: 12%-20%;
Al2O3/(%) Content: Not Less Than 85%;
Al2O3+MGO+Cr2o3 /(%): Not Less Than 93%;
Bubulk Density/(g/cm3): Not Lower Than 3.0;
Application: Core Components for Refining and Post-Furnace Trea;
|