| Specification |
Feature: Long Time Materials, Instant Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Round Neck Down;
Application: Large Casting;
Application2: Steel Casting;
Effect: Feeding;
Modulus: 1.8-8.3cm;
Materilas: Slurry;
Compressive Strength: >2.0;
Air Permeability: >30;
Generating Capacity of Heat: >3.5;
Thermal Peak: >1250;
Moisture: <1.0;
Type: Casting Accessories;
Material: Floating Beads;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, High Temperature Resistance;
Production Process: Casting Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Product Name: Heat Resistant Insulating Castable;
Cold Crushing Strength(MPa): 50~70MPa;
Keyword: Lightweight Refractory Castable;
Application: Industrial Furnaces;
Function: High Temperature Resistant;
Raw Material: Industrial Alumina Oxide Powder;
Package: Customizable;
Type: Refractory Material;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Anti-Stripping, Wear Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Product Name: Industrial Kiln High Alumina Lining Brick;
Apparent Porosity: Less Than 23%;
Bulk Density(Kg/M3): 2.0-2.5g/cm3;
Cold Crushing Strength(MPa): 40~70MPa;
Refractoriness Under Load (0.2MPa): Min 1470;
Keywords: Aluminum Fire Bricks;
Color: Yellow Firebrick;
Al2O3 Content (%): 48%-85%;
Type: Refractory Material;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Product Name: Mullite Insulation Birck;
Model Number: Jm23 Jm26 Jm28 Jm30 Jm32 Brick;
Al2O3(%): 80;
Refractoriness Under Load 0.2MPa(°c): >1450;
Keyword: Insulating Fire Brick;
Type: Refractory Material;
Material: Mullite;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Density: 0.6-1.3 Kg/M3;
Color: Yellowish Yellow;
|