| Specification |
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Module;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400c, 1260c;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Classification Temperature: 1260c;
Certifiacte: ISO9001:2000;
Bulk Density: 160-220 Kg/Cm3;
Al2O3: 44%;
Sio2: 52%;
Fe2o3+TiO2: 1.0%;
Thermal Conductivity@400c: 0.09W/M.K;
Thermal Conductivity@500c: 0.119W/M.K;
Thermal Conductivity@600c: 0.152W/M.K;
Linear Shrinkage After Heating: 2.5%@1000c*24h;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Corrosion Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Product Name: High Alumina Refractory Brick;
Apparent Porosity: Less Than 23%;
Bulk Density(Kg/M3): 2.0-2.5g/cm3;
Cold Crushing Strength(MPa): 40~70MPa;
Al2O3 Content (%): 48%-85%;
Keyword: High Temperature Kiln Refractory Bricks;
Model Number: Sk35,Sk36,Sk37,Sk38,Sk40;
Refractoriness Under Load (0.2MPa): Min 1420;
Color: Yellow Fire Brick;
Application: Industrial Furnaces;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Cylinder & Ball Shape;
Usage: Steel Industry;
Stock Condition: Should Be Stocked in Dry Condition;
Application: Steel Water Flow Control;
Key Words: Monoblock Stopper;
Size: Can Be Customized According to Customer Requiremen;
Advantage: High Safety/Accurate Flow Control/Stable Perform;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Cylinder & Ball Shape;
Usage: Steel Industry;
Stock Condition: Should Be Stocked in Dry Condition;
Application: Steel Water Flow Control;
Key Words: Monoblock Stopper;
Size: Can Be Customized According to Customer Requiremen;
Advantage: High Safety/Accurate Flow Control/Stable Perform;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Powder;
Type: Refractory Material;
Sample: Available;
Advantage: Long-Term Service;
Raw Material: Industrial Alumina Oxide Powder;
Keyword: Tundish Permanent Lining Castable;
Al2O3%: ≥60-70;
Material: Castable;
|