| Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Module;
Manufacturing Technique: Jilt Silk Rug;
Kind: Ordinary Ceramic Fiber;
Color: White;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Material: Alumina Silicate;
Thickness: 10mm~50mm;
Width: 610mm/1220mm;
Length: 3600mm, 7200mm, or Other Request;
Density: 70-128kg/M3;
Fiber Diameter (Um): 3-5;
Application: Ndustrial Furnace/High Temperature Equipment;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material;
Temprature Classification: 1900℃, 1600℃, 1500℃, 1400℃, 1260℃, 1050℃, 2200℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3, Zro2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Jilt Silk Rug;
Kind: Zirconia Fiber;
Zro2 +Hfo2(%): 89.74;
Y203(%): 10.06;
Pellet Content≥75μ(%): <2;
Appearance: White, Cotton Wool;
Mean Diameter: 200nm-400nm/800nm-1um/2-4um;
Fibrous Phase: Tetragonal;
Service Temperature: ≤2200℃;
Fusing Point: >2700℃;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material;
Temprature Classification: 1900℃, 1600℃, 1500℃, 1400℃, 1260℃, 1050℃, 2200℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3, Zro2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Jilt Silk Rug;
Kind: Zirconia Fiber;
Zro2 +Hfo2(%): 89.74;
Y203(%): 10.06;
Pellet Content≥75μ(%): <2;
Appearance: White, Cotton Wool;
Mean Diameter: 200nm-400nm/800nm-1um/2-4um;
Fibrous Phase: Tetragonal;
Service Temperature: ≤2200℃;
Fusing Point: >2700℃;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Chunking;
Manufacturing Technique: Blowing Spun;
Kind: Chrome+Zirconium;
Product Name: Ceramic Fiber Module;
Type: 1500c Chromium Zirconium Composite;
Classification Temperature: 1500c;
Product Keywords: Heat-Insulating;
Advantage: Regular Size, Easy to Install;
Color: Green and White;
Raw Material: Ceramic Fiber;
Length: as Per Customer's Request;
Width: as Per Customer's Request;
Thickness: as Per Customer's Request;
Bulk Density: 170-260(Kg/M3);
Design According to Drawing: Support;
Sample: Support;
Application: Refractory Furnace Lining Insulation Materials;
Feature: Low Thermal Conductivity;
|