| Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Color: White;
Density: 250-300 Kg/M3;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spun or Blown;
Kind: High Purity Ceramic Fiber;
Fiber Diameter(μm): 3.5;
Sio2: 50-52;
Working Temperature: 1100c, 1260c, 1300c, 1400c;
Dimensions: as Request;
Application: Ceramic Fiber Products;
Shrinkage (1800℉, 3h): 3;
|