| Specification |
Feature: Long Time Materials;
Refractoriness (℃): 1260c, 1360c, 1400c;
Shape: Ceramic Fiber Module;
Type: Heat-Resistant Material;
Material: Al2O3+Sio2;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, High-Temperature Resistant;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Al2O3: ≥48%;
Apparent Porosity: ≤23%;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, High Temperature Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Material: Castable;
Product Name: High Alumina Refractory Castable;
Color: Grey;
Sample: Provide;
Cold Crushing Strength(MPa): 50~70MPa;
Application: Industrial Furnaces;
Function: Functional Refractories;
Advantage: High Temperature Resistant;
Raw Material: Industrial Alumina Oxide Powder;
Maximum Service Temperature: 1200-1400;
Feature: Long Time Materials, Powder;
Type: Refractory Material;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, High Hardness Moderate Surface Roughness;
Production Process: Calcined;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Grain Size, Lump, Fine;
Advantage I: General Surface Treatment;
Advantage II: Moderate Grinding;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|