| Specification |
Feature: Long Time Materials;
Refractoriness (℃): 1050-1800c;
Shape: Plate;
Type: Heat-Resistant Material;
Material: Low Temperature Ceramic Fiber;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3(%): ≥55;
Fe2o3(%): ≤0.9;
Bulk Density(g/cm3): ≤0.95;
Cold Compressive Strength(MPa): ≥2.0;
Thermal Conductivity(350±25℃): ≤0.37;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3(%): ≥55;
Fe2o3(%): ≤0.9;
Bulk Density(g/cm3): ≤0.95;
Cold Compressive Strength(MPa): ≥2.0;
Thermal Conductivity(350±25℃): ≤0.37;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3(%): ≥55;
Fe2o3(%): ≤0.9;
Bulk Density(g/cm3): ≤0.95;
Cold Compressive Strength(MPa): ≥2.0;
Thermal Conductivity(350±25℃): ≤0.37;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3(%): ≥55;
Fe2o3(%): ≤0.9;
Bulk Density(g/cm3): ≤0.95;
Cold Compressive Strength(MPa): ≥2.0;
Thermal Conductivity(350±25℃): ≤0.37;
|