| Specification |
Classification: High-Alumina;
Feature: Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Paper;
Color: White;
Bulk Density: 170~220;
Compression Strength(MPa): 0.65~0.75;
Sio2: 44~53;
Type: Heat-Resistant Material;
Material: Alumina Silica;
|
Classification: Refractory Materials;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): Refractoriness<1580;
Shape: Plate;
Product Name: Alumina Ceramic Foam Filter;
Application: Aluminum Alloys and Others Nonferrous Metal Alloys;
Pore Density (Ppi): 10-40;
Operating Temperature: <1200 Celsius Degree;
Thickness: 12-25mm;
Porosity (%): 80-90;
Bending Strength (MPa): >0.6;
Compression Strength (MPa): >0.8;
Thermal Sgock Resistance (Times/1100): 6;
Color: White;
|
Classification: Refractory Materials;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): Refractoriness<1580;
Shape: Plate;
Product Name: Alumina Ceramic Foam Filter;
Application: Aluminum Alloys and Others Nonferrous Metal Alloys;
Pore Density (Ppi): 10-40;
Operating Temperature: <1200 Celsius Degree;
Thickness: 12-25mm;
Porosity (%): 80-90;
Bending Strength (MPa): >0.6;
Compression Strength (MPa): >0.8;
Thermal Sgock Resistance (Times/1100): 6;
Color: White;
|
Classification: Refractory Materials;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): Refractoriness<1580;
Shape: Plate;
Product Name: Alumina Ceramic Foam Filter;
Application: Aluminum Alloys and Others Nonferrous Metal Alloys;
Pore Density (Ppi): 10-40;
Operating Temperature: <1200 Celsius Degree;
Thickness: 12-25mm;
Porosity (%): 80-90;
Bending Strength (MPa): >0.6;
Compression Strength (MPa): >0.8;
Thermal Sgock Resistance (Times/1100): 6;
Color: White;
|
Classification: Refractory Materials;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): Refractoriness<1580;
Shape: Plate;
Product Name: Alumina Ceramic Foam Filter;
Application: Aluminum Alloys and Others Nonferrous Metal Alloys;
Pore Density (Ppi): 10-40;
Operating Temperature: <1200 Celsius Degree;
Thickness: 12-25mm;
Porosity (%): 80-90;
Bending Strength (MPa): >0.6;
Compression Strength (MPa): >0.8;
Thermal Sgock Resistance (Times/1100): 6;
Color: White;
|