| Specification |
Classification: Ceramic Fiber Board;
Feature: Good Thermal Insulation Performance, High-Temperature Resistant, Insulation Material;
Refractoriness (℃): 1100~1360;
Shape: Plate;
Al2O3: 52-55%;
Sio2: 52%;
Fe2o3: 1%;
Density: 260/320kg/M3;
Tensil Strength: 0.5MPa;
Standard Size: 600*400*20-50 900*600*20-50;
Rate of Thermal Conductivity (W/M.K): 0.132 (800℃) 0.180 (1000℃);
Rate of Linear (%): -4(1200º C);
Type: Refractory Material;
Material: Alumina Silicon;
|
Classification: Semi-Silica;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Bulk Density: 2.31~2.4G/Cm3;
Ai203 Content %): 22.5%;
Cao Content %): 2.5;
Acid Resistance: 99.8%;
Standard Size: 230*114*65mm;
Si02 Content %): 69.8%;
Si02(%): 69.8%;
High Working Temperature: 1650-1720c;
Application: Nonferrous Metal Furnace;
Single Package Size: 100X100X110.Cm;
|
Classification: Semi-Silica;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Bulk Density: 2.31~2.4G/Cm3;
Ai203 Content %): 22.5%;
Cao Content %): 2.5;
Acid Resistance: 99.8%;
Standard Size: 230*114*65mm;
Si02 Content %): 69.8%;
Si02(%): 69.8%;
High Working Temperature: 1650-1720c;
Application: Nonferrous Metal Furnace;
Single Package Size: 100X100X110.Cm;
|
Classification: Semi-Silica;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Bulk Density: 2.31~2.4G/Cm3;
Ai203 Content %): 22.5%;
Cao Content %): 2.5;
Acid Resistance: 99.8%;
Standard Size: 230*114*65mm;
Si02 Content %): 69.8%;
Si02(%): 69.8%;
High Working Temperature: 1650-1720c;
Application: Nonferrous Metal Furnace;
Single Package Size: 100X100X110.Cm;
|
Classification: Semi-Silica;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Bulk Density: 2.31~2.4G/Cm3;
Ai203 Content %): 22.5%;
Cao Content %): 2.5;
Acid Resistance: 99.8%;
Standard Size: 230*114*65mm;
Si02 Content %): 69.8%;
Si02(%): 69.8%;
High Working Temperature: 1650-1720c;
Application: Nonferrous Metal Furnace;
Single Package Size: 100X100X110.Cm;
|