| Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1900℃;
Chemical Composition:: Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Application: Liners of Industrial Furnace, Muffle Furnace Chamb;
Thickness: 10-50mm;
Width: 300/600/1000mm;
Length: 600/900/1000/1200mm;
Grade: HP (High Pure);
Ultimate Strength: 0.5MPa;
Working Temperature: 1100c;
Fiber Diameter: 3~5um;
Thermal Conductivitycti: 0.132(800c)/0.180(1000c);
Density: 280/300/320/350g/cm3;
Raw Material: Ceramic Fiber Bulk;
Shrinkage (1800℉, 3h): 3%(24h);
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: SiO2, SiC, Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Standard Density: 6, 8, 10 Lbs./Cu. FT. (96, 128, 160 Kg/M3);
Size: 7320 * 610/1220 * 25mm, 3660 * 610;
Standard Width: 24" and 48" (610/1220mm);
Standard Thickness: 1/4", 1/2", 1", 1-1/2", 2" (6/12.7/25/38/50mm);
Features: No Asbestos, Low Thermal Conductivity etc;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivitycompression Rebound: ≤ 0.153;
Raw Material: Ceramic Fibre Bulk;
Color: White;
Application: Refractory;
Phone: 15093300725;
Feature: Heat Resistant Insulation;
Classification Temperature: 1260;
Thermal Conductivity: >90;
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: SiO2, SiC, Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Standard Density: 6, 8, 10 Lbs./Cu. FT. (96, 128, 160 Kg/M3);
Size: 7320 * 610/1220 * 25mm, 3660 * 610;
Standard Width: 24" and 48" (610/1220mm);
Standard Thickness: 1/4", 1/2", 1", 1-1/2", 2" (6/12.7/25/38/50mm);
Features: No Asbestos, Low Thermal Conductivity etc;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivitycompression Rebound: ≤ 0.153;
Raw Material: Ceramic Fibre Bulk;
Color: White;
Application: Refractory;
Feature: Heat Resistant Insulation;
Classification Temperature: 1260;
Thermal Conductivity: >90;
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: SiO2, SiC, Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Standard Density: 6, 8, 10 Lbs./Cu. FT. (96, 128, 160 Kg/M3);
Size: 7320 * 610/1220 * 25mm, 3660 * 610;
Standard Width: 24" and 48" (610/1220mm);
Standard Thickness: 1/4", 1/2", 1", 1-1/2", 2" (6/12.7/25/38/50mm);
Features: No Asbestos, Low Thermal Conductivity etc;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivitycompression Rebound: ≤ 0.153;
Raw Material: Ceramic Fibre Bulk;
Color: White;
Application: Refractory;
Feature: Heat Resistant Insulation;
Classification Temperature: 1260;
Thermal Conductivity: >90;
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: SiO2, SiC, Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Standard Density: 6, 8, 10 Lbs./Cu. FT. (96, 128, 160 Kg/M3);
Size: 7320 * 610/1220 * 25mm, 3660 * 610;
Standard Width: 24" and 48" (610/1220mm);
Standard Thickness: 1/4", 1/2", 1", 1-1/2", 2" (6/12.7/25/38/50mm);
Features: No Asbestos, Low Thermal Conductivity etc;
Ultimate Strength (≥ MPa): 0.08-0.12MPa;
Shrinkage: 3h): 3%(24 Hours);
Thermal Conductivitycompression Rebound: ≤ 0.153;
Raw Material: Ceramic Fibre Bulk;
Color: White;
Application: Refractory;
Feature: Heat Resistant Insulation;
Classification Temperature: 1260;
Thermal Conductivity: >90;
|