| Specification |
Material: Acrylic;
Kind: Color Plastic;
Water Absorption: 0.12%~0.25%;
Contraction Percentage: 1.0%~2.5%;
Tensile Strength: 81~130MPa;
Grade: 100% Virgin;
Diameter: 2-350mm;
Density: 1.2g/cm3;
Place of Origin: China;
ODM: Yes;
OEM: Yes;
Color: White, Black, Red, Blue, Yellow;
|
Material: PE;
Kind: Plastic Bar;
Water Absorption: 0.2%~0.3%;
Contraction Percentage: ＜0.4%;
Tensile Strength: 41~50MPa;
Product Name: High Strength UHMWPE Round Bar;
Processing Service: Cutting/ Molding;
Mold Number: UHMWPE;
Purity: 100%;
Diameter: 10mm 20mm 30mm 50mm or Customized;
Length: 500mm 1000mm or Customized;
Density: 0.94 -0.96 g/cm3;
Working Temperature: -69℃ - 90℃;
Melting Temperature: 135℃-138℃;
Hardness: D659;
Molecular Weight: ≥6 Million G/Mol;
Elongation: 11%;
Application: Chemical, Engineering, Food, Medical;
MOQ: 100kg;
Package: Customized;
|
Material: PE;
Kind: Plastic Bar;
Water Absorption: 0.2%~0.3%;
Contraction Percentage: ＜0.4%;
Tensile Strength: 41~50MPa;
Product Name: High Strength UHMWPE Round Bar;
Processing Service: Cutting/ Molding;
Mold Number: UHMWPE;
Purity: 100%;
Diameter: 10mm 20mm 30mm 50mm or Customized;
Length: 500mm 1000mm or Customized;
Density: 0.94 -0.96 g/cm3;
Working Temperature: -69℃ - 90℃;
Melting Temperature: 135℃-138℃;
Hardness: D659;
Molecular Weight: ≥6 Million G/Mol;
Elongation: 11%;
Application: Chemical, Engineering, Food, Medical;
MOQ: 100kg;
Package: Customized;
|
Material: PVC;
Kind: Hard Plastic Rods;
Water Absorption: 0.2%~0.3%;
Contraction Percentage: 0.4%~1.4%;
Tensile Strength: 51~80MPa;
Name: PVC Rod;
Other Name: Polyvinyl Chloride Rod;
Size: Customizable;
Purity: 100%;
Processing Method: Extrusion/Molding;
Color: White,Green, Red, Yellow, Black;
Weather Resistance: Excellent;
Impact Resistance: Excellent;
Electrical Insulation: Excellent;
Shipping Method: Sea/Air/Rail;
MOQ: 100kg;
Delivery Time: Stock;
MSDS: Available;
COA: Available;
Sample: Available;
|
Material: PVDF;
Kind: Plastic Bar;
Water Absorption: ＜0.01%;
Contraction Percentage: ＜0.4%;
Tensile Strength: 41~50MPa;
Density: 1.78g/Cm³;
Temperature Range: -30-150 Degree C;
Sample: Free;
Elongation at Break: 300-450%;
|