| Specification |
Bulk Density: 1.82g;
Type: Graphite Mold;
Carbon Content: High-Carbon;
Grade: Industrial Grade;
Forming Way: Molded Graphite;
Crystal Morphology: Flake Graphite;
Composition: 100% Carbon;
|
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Product Name: Graphite Box;
Keywords: Graphite Mold;
Grain Size (≤μm): 25;
Bulk Density (≥g/cm3): 1.78-1.9;
Compressive Strength (≥MPa): 70-90;
Flexural Strength(≥MPa): 35-42;
Porosity(≤%): 17-11;
Specific Resistance(≤μωM): 12-10;
Ash Content(≤Ppm): 600-300;
Shore Hardness: 50-60;
|
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Product Name: Graphite Box;
Keywords: Graphite Mold;
Grain Size (≤μm): 25;
Bulk Density (≥g/cm3): 1.78-1.9;
Compressive Strength (≥MPa): 70-90;
Flexural Strength(≥MPa): 35-42;
Porosity(≤%): 17-11;
Specific Resistance(≤μωM): 12-10;
Ash Content(≤Ppm): 600-300;
Shore Hardness: 50-60;
|
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Product Name: Graphite Box;
Keywords: Graphite Mold;
Grain Size (≤μm): 25;
Bulk Density (≥g/cm3): 1.78-1.9;
Compressive Strength (≥MPa): 70-90;
Flexural Strength(≥MPa): 35-42;
Porosity(≤%): 17-11;
Specific Resistance(≤μωM): 12-10;
Ash Content(≤Ppm): 600-300;
Shore Hardness: 50-60;
|
Application Area: Automobile Industry, Electronic Industry;
Feature: Corrosion Resistance, High-Thermal Conductivity, Thermal Shock Resistance;
Manufacturing Technique: Pressing And Sintering;
Product Name: Graphite Box;
Keywords: Graphite Mold;
Grain Size (≤μm): 25;
Bulk Density (≥g/cm3): 1.78-1.9;
Compressive Strength (≥MPa): 70-90;
Flexural Strength(≥MPa): 35-42;
Porosity(≤%): 17-11;
Specific Resistance(≤μωM): 12-10;
Ash Content(≤Ppm): 600-300;
Shore Hardness: 50-60;
|