| Specification |
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): Refractoriness<1580;
Shape: Brick;
Al2O3: 35-42%;
Apparent Porosity: 20-26%;
Cold Crushing Strength: 30-45MPa;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Methord;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: 1QC Ladle Slide Gate Plate with Collector Nozzle;
Al2O3: 85% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Hot Sales Area: Pakistan;
Function: Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): Refractoriness<1580;
Shape: Plate;
Product Name: Alumina Ceramic Filter Plate;
Type: Refractory Material;
Useful: Aluminium Liquid Filtration;
Application: Aluminum Alloys and Other Nonferrous Metal Alloys;
Pore Density (Ppi): 8-60;
Porosity (%): 80-90;
Bending Strength(MPa): >1.0;
Compression Strength(MPa): >0.8;
Thermal Sgock Resistance(Times/1100): 6;
Sealing Gasket: Fiber Paper, Fiber Cotton and Expandable Cotton;
|