| Specification |
Classification: High-Alumina;
Feature: Good Mechanical Strength, High-Temperature Resistant;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Sio2: 37%~45%;
Bulk Density: ≤2.3G/Cm3;
Al2O3: ≥50%;
Fe2o3: ≤1.2%;
|
Feature: High Temperature Resistant;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Cell Shape: Square, Hexagon, Circular, Triangle, etc.;
Cell Number: 13-60 Cell;
Groove: Plate, Single, Double, Cross, Four Footer, Chute;
Material: Alumina Block;
Type: Honeycomb Ceramic Thermal Storage Media;
|
Feature: High Temperature Resistant;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Cell Shape: Square, Hexagon, Circular, Triangle, etc.;
Cell Number: 25*25, 32*32, 40*40, 43*43, 50*50 Cell;
Groove: Plate, Single, Double, Cross, Four Footer, Chute;
Type: Honeycomb Ceramic Thermal Storage Media;
Material: Alumina/Cordierite/Mullite/Corundum;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Pipe;
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Ceramic;
Color: White;
Size: Customer Requirements;
Chemical Composition: Alumina;
Bending Strength: 40MPa-70MPa;
Bulk Density: 2.5-2.9g/cm3;
Usage: Ceramic Kiln;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|