| Specification |
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Paper;
Color: White;
Density (Kg/M3): 180-220;
Chemical Composition: Al2O3 Sio2;
Type: Heat-Resistant Material;
Material: Aluminium Silicate;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Usage: Furnace Liner;
Al203 Content (%): 35%-45%;
Si02 Content (%: 52%;
MGO Content (%): 0.1%;
Refractoriness (Degree): Common1580< Refractoriness< 1770;
Cro Content %): 0.1%;
Bulk Density: 2.0~2.2g/cm3;
Sic Content %): 0.1%;
Apparent Porosity: 23%~26%;
Cold Crushing Strength: 20~35MPa;
Cao Content %): 0.1%;
Application: Industrial Furnaces;
Single Package Size: 100X100X110.Cm;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Cao Content %: 3;
Al203 Content (%): 45;
Si02 Content (%: 10%;
Refractoriness (Degree): Common1580< Refractoriness<1770;
Material: Alumina Cement;
Water Required for Casting %: 5-9;
Cao: 2-3%;
Bulk Densityg/Cm3): 2.4-3.0;
Ai203: 45-95%;
Application: Furnace Lining;
Fe203: 1.5-2.4;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Cao Content %: 3;
Al203 Content (%): 45;
Si02 Content (%: 10%;
Refractoriness (Degree): Common1580< Refractoriness<1770;
Material: Alumina Cement;
Water Required for Casting %: 5-9;
Cao: 2-3%;
Bulk Densityg/Cm3): 2.4-3.0;
Ai203: 45-95%;
Application: Furnace Lining;
Fe203: 1.5-2.4;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Cao Content %: 3;
Al203 Content (%): 45;
Si02 Content (%: 10%;
Refractoriness (Degree): Common1580< Refractoriness<1770;
Material: Alumina Cement;
Water Required for Casting %: 5-9;
Cao: 2-3%;
Bulk Densityg/Cm3): 2.4-3.0;
Ai203: 45-95%;
Application: Furnace Lining;
Fe203: 1.5-2.4;
|