| Specification |
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): Over 1580 Deg C;
Shape: Block;
Color: White;
Shape: Rectangular;
Application: Metallurgy, Ceramic, Casting, Glass;
Material: Alumina, Quartz, Mullite, Corundum;
Temperature: 1800ºC;
|
Feature: Long Time Materials;
Refractoriness (℃): Refractoriness> 2000;
Shape: Powder;
Al2O3: 60-90;
Fe2o3: Min1.8;
TiO2: Min 4.0;
K2o+Na2o: Min 0.25;
Cao+MGO: Min0.5;
Bulk Density: Max 3.30;
Sample: Free;
Factory History: 8 Years;
Application: Refractory;
Color: Yellow/Dark Gray/Dark Blue;
Raw Material: Bauxite Ore;
Cro Content: Trace;
Term Payment: Tt;
Delivery Time: 7-15days;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Material: Alumina Block, Castable;
Al2O3 Content (%): 42~90;
Cao Content (%): Lillte;
Cro Content (%): 0.1~0.3%;
Usage: Furnace Liner;
Sio2 Content: 0.1max;
Sic Content (%): 1.2-1.4%;
Color: Gray;
Keyword: Refractories Low Cement Castables;
Fe2o3: 1.35-2.3%;
Advantage: Life Long;
Flexural Strength MPa: 6h;
Sample: Free;
Factory History: 8years;
Type: Refractory Material;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Melting Point;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Material: Alumina Block, Castable;
Al2O3 Content (%): 42~90;
Cao Content (%): Lillte;
Cro Content (%): 0.1~0.3%;
Usage: Furnace Liner;
Sio2 Content: 0.1max;
Sic Content (%): 1.2-1.4%;
Color: Gray;
Keyword: Refractories Low Cement Castables;
Fe2o3: 1.35-2.3%;
Advantage: Life Long;
Flexural Strength MPa: 6h;
Sample: Free;
Factory History: 8years;
Type: Refractory Material;
|
Feature: Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Material: Alumina Block, Castable;
Al2O3 Content (%): 42~90;
Cao Content (%): Lillte;
Cro Content (%): 0.1~0.3%;
Usage: Furnace Liner;
Sio2 Content: 0.1max;
Sic Content (%): 1.2-1.4%;
Color: Gray;
Keyword: Refractories Low Cement Castables;
Fe2o3: 1.35-2.3%;
Advantage: Life Long;
Flexural Strength MPa: 6h;
Sample: Free;
Factory History: 8years;
Type: Refractory Material;
|