| Specification |
Color: Pink;
Appearance: Powder;
Method: Spray;
Substrate: Steel;
|
Color: Any Color;
Appearance: Powder;
Main Raw Material: Resin;
Paint Film Property: According to Customer Requests;
Method: Spray;
Level: Finish Coat;
Category: According to Customer Requests;
Substrate: Metals(Aluminum/Iron/Steel);
Components: Film Forming Matter;
Formation Mechanism: Non Conversion Type;
|
Color: PAL/Pantone;
Appearance: Powder;
Main Raw Material: Epoxy;
Paint Film Property: Corrosion Protection;
Method: Spray;
Level: Finish Coat;
Category: One-Component Paint;
Substrate: Metal;
Components: Film Forming Matter;
Curing Time: 10 Min;
Curing Temperature: 200℃;
Density: 1.2 - 1.8 G/Cm³;
Particle Size Distribution: Over-Sieving Rate ≥ 98% (180 Mesh);
Curing Conditions: 180 - 200℃ / 10 - 15 Minutes;
Film Thickness Range: 60 - 120 μm;
Adhesion: 0 Grade (Grid Test Method);
Impact Strength: ≥ 50 Kg·Cm;
Salt Spray Resistance: ≥ 500 Hours (No Blistering or Peeling);
Weather Resistance: ≥ 1000 Hours (Lightfastness > 80%);
|
Color: Customized;
Appearance: Powder;
Main Raw Material: Epoxy Polyester;
Paint Film Property: Conducting Paint;
Method: Spray;
Level: Finish Coat;
Category: Thermosetting Poeder Coating;
Substrate: Sheet Metal;
Components: Polyester Resin, Curing Agent, Pigment, Assistant;
Formation Mechanism: Conversion Type;
Features: Anti-Corrosion, Temperature Resistance;
Gloss: High Gloss, Low Gloss;
Leat Time: 3-15days;
N.W: 25kg;
Application: Metal Surface;
Curing Condition: 180-200 Degree/8-10 Minutes;
Impact: 50cm.Kg;
Adhesion: 0 Level;
Salt Spray Test: 500h;
Bending Test: <3mm;
|
Color: Customized;
Appearance: Powder;
Main Raw Material: Epoxy Polyester;
Paint Film Property: Conducting Paint;
Method: Spray;
Level: Finish Coat;
Category: Thermosetting Poeder Coating;
Substrate: Sheet Metal;
Components: Polyester Resin, Curing Agent, Pigment, Assistant;
Formation Mechanism: Conversion Type;
Features: Anti-Corrosion, Temperature Resistance;
Gloss: High Gloss, Low Gloss;
Leat Time: 3-15days;
N.W: 25kg;
Application: Metal Surface;
Curing Condition: 180-200 Degree/8-10 Minutes;
Impact: 50cm.Kg;
Adhesion: 0 Level;
Salt Spray Test: 500h;
Bending Test: <3mm;
|