| Specification |
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Particle Size Specification: 0-1mm, 1-3mm, 3-5mm, 5-8mm, 100m, 200m, 325m, All;
Purpose: Refractory Materials, Ceramics, Metallurgy, Castin;
Chemical Formula: 3Al2O3·2sio2;
Item/Grade: M45 M47 M60 M70 Ect;
Size Specifications: Size Specifications: 0-1mm, 1-3mm, 3-5mm, 5-8mm, 1;
Al2O3: 42-78%;
Sio2: 20-50%;
Fe2o3: 1% Max;
Na2o: 0.5%Max;
TiO2: 2.6%Max;
MGO: 0.3%Max;
K2o: 0.5% Max;
Bulk Density: ≥2.45;
Water Absorption: 3max;
|
Classification: Clay;
Feature: Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 35-80%;
Fe2o3: 1.5-3.0%;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 30-100 MPa;
Working Temperature: 1200~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Sk32/Sk34/Sk35/Sk36/Sk37/Sk38;
Refractoriness Under Load (0.2MPa): 1350-1700 ºC;
Color: Yellow;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Usage: Filter Material, High Temperature Insulating Material, Industrial Ceramic;
Chemical Composition: Al2O3.Sio2;
Temprature Classification: 1350℃;
Shape: Square, Hexagon, Circular, Triangle, etc.;
Kind: Industry Ceramic;
Bulk Density(Kg/M3): 500-680;
Middle Wall Thickness(mm): 0.3;
Thermal Expansion Coefficient(in/Ink): 1.5- 1.8;
Thermal Shock Resistance (K): Max 500;
Height(mm): 50;
Average Weight Per Piece(Kg): 0.3;
Specific Heat Capacity(J/Kgk): 850- 1000;
Water Absorption %: 20-25;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Chemical Composition: Al2O3.Sio2;
Temprature Classification: 1350℃;
Kind: Industry Ceramic;
Bulk Density(Kg/M3): 500-680;
Middle Wall Thickness(mm): 0.3;
Thermal Expansion Coefficient(in/Ink): 1.5- 1.8;
Thermal Shock Resistance (K): Max 500;
Height(mm): 50;
Average Weight Per Piece(Kg): 0.3;
Specific Heat Capacity(J/Kgk): 850- 1000;
Water Absorption %: 20-25;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Usage: Filter Material, High Temperature Insulating Material, Industrial Ceramic;
Chemical Composition: Al2O3.Sio2;
Temprature Classification: 1350℃;
Shape: Square, Hexagon, Circular, Triangle, etc.;
Kind: Industry Ceramic;
Bulk Density(Kg/M3): 500-680;
Middle Wall Thickness(mm): 0.3;
Thermal Expansion Coefficient(in/Ink): 1.5- 1.8;
Thermal Shock Resistance (K): Max 500;
Height(mm): 50;
Average Weight Per Piece(Kg): 0.3;
Specific Heat Capacity(J/Kgk): 850- 1000;
Water Absorption %: 20-25;
|