| Specification |
Casting Method: Low Pressure Casting;
Casting Form Material: Metal;
Casting Metal: Aluminum Alloy;
Casting Form Usage Count: Permanent;
Surface Treatment: Sand Blast;
Surface Roughness: Ra3.2;
Coating: Zinc oxide;
Machining Tolerance: +/-0.01mm;
Standard: ASTM;
Elongation: 3.5%;
Tensile Strength: 280MPa;
Yield: 220MPa;
Coaxiality: 0.02;
Rotate Speed: 1500rpm;
Hardness: Hb85;
Weight: 40kg;
Heat Treatment: T6;
Service: OEM;
|
Casting Method: Investment Casting;
Casting Form Material: Metal;
Casting Metal: Cast Steel;
Casting Form Usage Count: Permanent;
Surface Treatment: Polishing;
Surface Roughness: Ra0.8;
Machining Tolerance: +/-0.01mm;
Standard: ASME;
Material: Stainless Steel;
Max Tolerance: 0.01mm;
Connection: Female;
Treatment: Surface Polishing;
|
Casting Method: Iron Casting;
Casting Form Material: Ggg50, Option Ggg60, ASTM80-55-06;
Casting Metal: Cast Iron;
Casting Form Usage Count: Permanent;
Surface Treatment: Dacromat Coating, Finish Painting;
Surface Roughness: Ra25-100;
Coating: Zinc oxide;
Machining Tolerance: 0.005mm-0.01mm-0.1mm;
Standard: According to Customer Requirement;
Material: Ggg50, Option Ggg60, ASTM80-55-06;
Blank Process: Iron Casting;
Casting Tolerance: CT9-11;
Machining Process: Drilling, Milling, Boring etc.;
Rough Surface Roughness: Ra25-100;
Casting Blank Weight: Range From 0.01kg-1000kg;
Lead Time: 45 Days for Tractor Part;
Service: OEM, ODM for Tractor Part;
Casting Blank Size: as Customer Request;
Specfication: as Customer Drawings;
|
Casting Method: Iron Casting;
Casting Form Material: Ggg50, Option Ggg60, ASTM80-55-06;
Casting Metal: Cast Iron;
Casting Form Usage Count: Permanent;
Surface Treatment: Dacromat Coating, Finish Painting;
Surface Roughness: Ra25-100;
Coating: Zinc oxide;
Machining Tolerance: 0.005mm-0.01mm-0.1mm;
Standard: According to Customer Requirement;
Material: Ggg50, Option Ggg60, ASTM80-55-06;
Blank Process: Iron Casting;
Casting Tolerance: CT9-11;
Machining Process: Drilling, Milling, Boring etc.;
Rough Surface Roughness: Ra25-100;
Casting Blank Weight: Range From 0.01kg-1000kg;
Lead Time: 45 Days for Turbo Exhaust Manifold;
Service: OEM, ODM for Turbo Exhaust Manifold;
Casting Blank Size: as Customer Request;
Specfication: as Customer Drawings;
|
Casting Method: Iron Casting;
Casting Form Material: Ggg50, Option Ggg60, ASTM80-55-06;
Casting Metal: Cast Iron;
Casting Form Usage Count: Permanent;
Surface Treatment: Dacromat Coating, Finish Painting;
Surface Roughness: Ra25-100;
Coating: Zinc oxide;
Machining Tolerance: 0.005mm-0.01mm-0.1mm;
Standard: According to Customer Requirement;
Material: Ggg50, Option Ggg60, ASTM80-55-06;
Blank Process: Iron Casting;
Casting Tolerance: CT9-11;
Machining Process: Drilling, Milling, Boring etc.;
Rough Surface Roughness: Ra25-100;
Casting Blank Weight: Range From 0.01kg-1000kg;
Lead Time: 45 Days for Iron Casting Valve Cover;
Service: OEM, ODM for Iron Casting Valve Cover;
Casting Blank Size: as Customer Request;
Specfication: as Customer Drawings;
|