| Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Grit / Powder/ Grain;
Name: White Fused Alumina;
Other Name: White Corundum;
Application: Refractories, Abrasives, Ceramics, Grindings;
Color: White;
Advantages: Factory;
Grain Size: F24-F220 /24#-220#/ 0-1mm, 1-3mm, 3-5mm/ 240#-10000#;
Type: Refractory Material;
Material: Alumina;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Casting High Temperature Firing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Product Name: Ladle Purging Plugs for Stiring Steel Molten;
Type 1: Slit/Slot Type Purge Plug;
Type 2: Porous Purge Plug;
Type 3: Segment /Plate Purge Plug;
Type 4: Preassembled Purge Plug and Well Block;
Types: Cleaning Plugs and Related Systems;
Metallurgical Needs: Different Refining Processes (Rh, Lf, Vd, VOD, Va;
Raw Material of Slit Type: Chromite Corundum Spinel or Corundum Spinel;
Main Feature: High Blowing Rate;
Advantage: Easyier for Operation Control During Refining Proc;
Flow Rate Range: 12%-20%;
Al2O3/(%) Content: Not Less Than 85%;
Al2O3+MGO+Cr2o3 /(%): Not Less Than 93%;
Bubulk Density/(g/cm3): Not Lower Than 3.0;
Application: Core Components for Refining and Post-Furnace Trea;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Snref B60 Refractory High Quality Slide Gate Plat;
Material: Al-Zr-C or Al-C;
Brand: Sinorefractory /Snref;
Main Element: Alumina&Zirconia&Carbon;
Application: Ladle of Steel Mill;
Process: Shaped-Dry-High Temperature Firing-Pitch Immersed-;
Flatness of Sliding Surface: Less Than 0.05mm;
Feature 1: High Mechanical Strength;
Feature 2: High Resistance;
Feature 3: Excellent Oxidation Resistance;
Feature 5: Good Thermal Shock Stability;
Service Life: 4-8 Heats;
Usage Area: Continuous Casting in Steel Plant;
Workmanship: High Temperature Deep Burnt;
Other Material Type: Al-C or MGO Spinel Slide Plates;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: CS60 High-Temperature Resistant Slide Gate Nozzle;
Material: Al2O3+Zro2+C;
Brand: Sinorefractory /Snref;
Main Element: Alumina&Zirconia&Carbon;
Application: Ladle of Steel Mill;
Process: Shaped-Dry-High Temperature Firing-Pitch Immersed-;
Flatness of Sliding Surface: Less Than 0.05mm;
Feature 1: High Mechanical Strength;
Feature 2: High Resistance;
Feature 3: Excellent Oxidation Resistance;
Feature 5: Good Thermal Shock Stability;
Service Life: 4-8 Heats;
Usage Area: Continuous Casting in Steel Plant;
Workmanship: High Temperature Deep Burnt;
Other Material Type: Al-C or MGO Spinel Slide Plates;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Refractory Snref Ladle Slide Gate Plate in Iron-St;
Material: Al-Zr-C or Al-C;
Brand: Sinorefractory /Snref;
Main Element: Alumina&Zirconia&Carbon;
Application: Ladle of Steel Mill;
Process: Shaped-Dry-High Temperature Firing-Pitch Immersed-;
Flatness of Sliding Surface: Less Than 0.05mm;
Feature 1: High Mechanical Strength;
Feature 2: High Resistance;
Feature 3: Excellent Oxidation Resistance;
Feature 5: Good Thermal Shock Stability;
Service Life: 4-8 Heats;
Usage Area: Continuous Casting in Steel Plant;
Workmanship: High Temperature Deep Burnt;
Other Material Type: Al-C or MGO Spinel Slide Plates;
|